Abstract
A highly accurate prediction of hermeticity lifetime is made for eutectic 63Sn37Pb and 80Au20Sn alloy solder sealed optical fiber-Kovar/sup TM/ nosetube feedthroughs subjected to repetitive thermal cycling. Thermal fatigue fracture of the Sn-Pb solder/Kovar/sup TM/ interface develops when cracks, initially generated from creep deformation of the solder, propagate gradually through the junction in the axial direction. A nonlinear axisymmetric finite element analysis of the 63Sn37Pb fiber feedthrough seal is performed using a thermo-elastic creep constitutive equation, and solder joint fatigue based on accumulated strain energy associated with solder creep imposed by temperature cycling is analyzed. Additionally, thermal effective stress and plastic strain is studied for alternative 80Au20Sn solder by the finite element method with results indicating significant increase in useful life as compared to 63Sn37Pb. SEM/EDX metallurgical analysis of the solder/Ni-Au plated Kovar/sup TM/ nosetube interface indicates that AuSn/sub 4/ intermetallic formed during soldering with 63Sn37Pb also contributes to joint weakening, whereas no brittle intermetallic is observed for 80Au20Sn. Hermetic carbon coated optical fibers metallized with Ni,P-Ni underplate and electrolytic Au overplating exhibit correspondingly similar metallurgy at the solder/fiber interface. Combined hermeticity testing and metallurgical analysis carried out on 63Sn37Pb and 80Au20Sn alloy solder sealed optical fiber feedthroughs after repetitive temperature cycling between -65 and +150/spl deg/C, and -40 and +125/spl deg/C validated the analytical approach.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.