Abstract
Cellulose triacetate (CTA) nanofibers were formed by electrospinning using two binary solvent systems: methylene chloride/ethanol and chloroform/acetone. Previously, licorice root cellulose (LRC) with a degree of polymerization (DP) of 710 was extracted from licorice root waste by alkaline treatment and hydrogen peroxide bleaching at high temperatures. Then CTA with a degree of substitution (DS) of 2.9 and an average molecular weight of 175 kDa was synthesized from LRC using acetic acid and acetic anhydride, sulfuric acid was as a catalyst. The influence of the electrospinning process and various solvent systems on the morphology and structure of nanofibers is studied. The structure and morphology of the nanofibers were characterized by Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction, scanning electron microscopy (SEM), thermal gravimetric analysis (TGA), and the sorption characteristics were also investigated. The results showed that the morphology and structure of nanofibers depended on the solvent mixture used. The average diameters of the CTA nanofibers with grooved morphology varied 200-700 nm (solvent methylene chloride/ethanol) and the dumbbell-shaped (flat ribbon) CTA nanofibers in a wide range from 200 nm to 4 mkm (solvent chloroform/acetone).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.