Abstract
Ce-incorporated MCM-41 mesoporous molecular sieves (CeMCM-41) were synthesized by microwave irradiation method from sodium silicate and ammonium cerium (IV) nitrate precursors and using cetyltrimethyl ammonium bromide (CTAB) as template. The resulting samples were characterized by means of XRD, TEM, FT-IR, UV-Vis, XPS and N2 physical adsorption, respectively. The effect of the Si/Ce molar ratio on the textural properties of CeMCM-41 was investigated. The results reveal that the CeMCM-41 was successfully synthesized. The resultant mesoporous materials have specific surface areas in the range of 602–1,216 m2/g and pore sizes in the range of ca. 2.6–2.9 nm. The structural properties are related to the amount of cerium incorporation. The surface area and pore volume of the resulting CeMCM-41 were gradually reduced as the cerium content in the sample increased, and the mesoporous ordering diminished.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.