Abstract
The phase structure and piezo/dielectric properties of xPb(In 1/2Nb 1/2)O 3– yPb(Mg 1/3Nb 2/3)O 3– zPbTiO 3 (PIN–PMN–PT x/ y/ z) ternary ceramics with morphotropic phase boundary (MPB) composition were investigated. It was found that Curie temperatures of choosing composition changed from 165 °C to 293 °C and the piezoelectric properties are almost the same at room temperature in PIN–PMN–PT system near MPB. The piezoelectric coefficient d 33 and electromechanical coupling factor k p are higher than 440 pC/N and 60%, respectively. Temperautre and dc bias dependence of piezoelectric response for PIN–PMN–PT ceramics were measured. The usage temperature range was found to be improved, compared with PMN–PT single crystal near MPB.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.