Abstract
Titanium dioxide (TiO2) thin film photocatalysts for the elimination of nitrogen oxides (NOx) were prepared by the dip-coating process using the sol–gel method. To prepare the sols, titanium (IV) butoxide (Ti(OBu)4), diethanolamine (DEA), butanol, and HCl were chosen. The TiO2 coatings were prepared using sols with varying volume ratios of Ti(OBu)4:DEA:Butanol. Additionally, three withdrawal speeds from the sol were employed. Subsequently, the TiO2 thin films were sintered at 500 and 700 °C. The obtained thin films were characterized using SEM to determine thickness, AFM to determine roughness, and the Step 500 platform for the adhesion test. NOx was found to be efficiently eliminated by TiO2 thin film photocatalyst. It is possible to obtain a TiO2 coating that is capable of degrading 300 ppb of NO in real time under specific conditions: a relative humidity of 30 %, a UV intensity of 20 W/m2, a gas flow rate of 1 dm3/min.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.