The magnetic hard-soft CoFe2O4–CoFe2 nanocomposite microfibers have been synthesized by the sol–gel and partial reduction process, where CoFe2O4 ferrite is the hard phase with a grain size range from 43 to 62 nm and CoFe2 alloy the soft phase with grain sizes around 30 nm. These nanocomposite microfibers exhibit the magnetization behavior like a single phase magnetic material, and the magnetic exchange coupling effects are observed between the hard and soft phases. The specific saturation magnetization of CoFe2O4–CoFe2 nanocomposite microfibers shows an increase tendency with the increasing weight fraction of CoFe2, while the coercivity is consequently reduced. The nanocomposite microfibers have a maximum remanence 51.7 Am2/kg when the phase contents of CoFe2 around 28 wt% and CoFe2O4 about 72 wt%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.