Abstract
Vanadium oxide thin films were grown on glass substrates using spray pyrolysis technique. The effects of substrate temperature, vanadium concentration in the initial solution and the solution spray rate on the nanostructural and the electrochromic properties of deposited films are investigated. Characterization and the electrochromic measurements were carried out using X-ray diffraction, scanning electron microscopy and cyclic voltammogram. XRD patterns showed that the prepared films have polycrystalline structure and are mostly mixed phases of orthorhombic α- V 2 O 5 along with minor β- V 2 O 5 and V 4 O 9 tetragonal structures. The preferred orientation of the deposited films was found to be along [101] plane. The cyclic voltammogram results obtained for different samples showed that only the films with 0.2 M solution concentration, 5 ml/min solution spray rate and 450°C substrate temperature exhibit two-step electrochromic properties. The results show a correlation between cycle voltammogram, morphology and resistance of the films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.