Abstract
Abstract Diluted magnetic semiconductors GaFeAs were grown by molecular beam epitaxy and characterized. Ga 1− x Fe x As ternary alloys were obtained at the growth temperature T s =200 °C ranging from x =0.005 to 0.03. The effects of thermal treatment on behaviors of defects, affecting to the magnetic properties of GaFeAs layer were particularly elucidated. As-grown samples were annealed at temperatures varying from 400 to 600 °C. From the measurement of double crystal X-ray diffraction, we observed Fe-related peak which shifted to a higher diffraction angle as the Fe content increased, indicating that the lattice constant decreases with increasing Fe content. In contrast, above the annealing temperature 500 °C, the lattice constant becomes smaller than that of GaAs. Using the deep level transient spectroscopy, various defects in GaFeAs layer were observed and identified in conjunction with magnetic properties.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.