Abstract
Indium tin oxide, which is used as transparent conducting layer in flexible device, is deposited on PET film by a magnetron sputtering in 300 mm wide roll-to-roll process (vacuum web coating). Sheet resistance, specific resistance and transmittance is differed by sputtering parameters such as working pressures, oxygen partial pressure, and thickness of ITO layer. ITO layer is deposited about 90 nm at roll speed of 0.24 m/min and its sputtering power is 3 kW. From the XRD spectrum deposited ITO layer is verified as amorphous. Under working pressure varied from to , sheet resistance is lowest at the working pressure of and its value is from to at the thickness of 90 nm. Oxygen partial pressure also varies sheet resistance and is optimized at the regime from 0.2% () to 0.6% (). In this oxygen partial pressure sheet resistance is lower than . As ITO layer thickness increases, sheet resistance decreases down to and specific resistance is about in 340 nm thickness ITO layer. Transmittance is measured at the wavelength of 550 nm and is about 90% for 180 nm thickness ITO/PET.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.