Abstract
A nitriding process based on two distinct nitrogen glow discharge modes, with sample temperatures ranging from 380 0C to 480 0C, was employed to treat the surface of austenitic stainless steel (SS 304). The temperature is controlled exclusively by switching the operation conditions of the discharges. First mode of operation is the conventional one, named cathodic, which runs at higher pressure values (1 mbar) in comparison to the second mode, named anodic, which runs at the pressure range of 10-3 - 10-2 mbar. Cathodic mode is used to quickly heat the sample holder, by the high ion flux. On the other hand, in the anodic mode, due to the lower operation pressure, higher effective ion acceleration takes place, which allows deeper ion implantation into the sample surface. This hybrid process was thoroughly explored regarding the duty cycle and conditions of operation, to achieve optimal performance of the treatments, which led to the attainment of surface hardness for samples of AISI SS 304 as high as 20 GPa and improvements including higher elastic modulus and resistance against corrosion. Detailed comparison among samples treated by this process with others treated by conventional method was done using nanoindentation, Auger Electron Spectroscopy (AES) and corrosion resistance testing.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.