Abstract
This study is focused on the electrochemical performance of perovskite-type materials based on doped LaGaO 3. La 0.8Sr 0.2Ga 0.8Mg 0.2O 3− δ (LSGM) and La 0.8Sr 0.2Ga 0.8Mg 0.115Co 0.085O 3− δ (LSGMC) were used as electrolytes and (Pr 0.7Ca 0.3) 0.9MnO 3 (PCM) and La 0.75Sr 0.25Cr 0.5Mn 0.5O 3− δ (LSCM) as cathode and anode material, respectively. LSGM and LSGMC electrolytes were prepared by tape casting with a thickness of about 600 μm. The performance of LSCM/LSGMC/PCM was slightly superior to that obtained on LSCM/LSGM/PCM at different temperatures in both humidified hydrogen and ethanol steam atmospheres, good values of power output in LSCM/LSGMC/PCM were 182 and 169 mW cm −2 using humidified hydrogen and ethanol steam as fuel, respectively, and oxygen as oxidant at 850 °C. Cell stability tests indicate no significant degradation in performance after 60 h of cell testing when LSCM anode was exposed to ethanol steam at 750 °C. Almost no carbon deposits were detected after testing in ethanol steam at 750 °C for >60 h on the LSCM anodes, suggesting that carbon deposition was limited during cell operation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.