Abstract

One of the problems in thin wall ductile iron (TWDI) fabrication is skin formation during the casting. The presence of this skin will decrease strength and strain of the TWDI. One of the ways to control this skin formation is to change the cooling rate during the process through a mold coating. In testing the effectiveness of skin prevention, the following variables were used for the mold coating i.e. (i) graphite: (ii) zirconium; and (iii) double layer of graphite-zirconium. After the process, the plates were characterized by non-etching, etching, tensile test, and SEM observation. The results showed that the average skin formation using graphite: 65 µm; zirconium: 13.04 µm; and double layer of graphite-zirconium: 33.25 µm. It seems that zirconium has the most effect on the skin prevention due to sulfur binding and magnesium locked, which then prevented rapid cooling resulting in less skin formation. The results also showed the number of nodules obtained in specimen with graphite: 703 nodules/mm2 with average diameter of 12.57 µm, zirconium: 798 nodules/mm2 with average diameter of 12.15 µm, and double layer of graphite-zirconium: 697 nodules/mm2 with average diameter of 11.9 µm and nodularity percentage of 82.58%, 84.53%, and 84.22%, respectively. Tensile test showed that the strength of the specimen with graphite is 301.1 MPa, with zirconium is 388.8 MPa, and with double layer of graphite-zirconium is 304 MPa. In overall, zirconium give the best performance on the skin formation prevention in TWDI fabrication.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call