Abstract
Abstract The effect of the simultaneous presence of nano- and micro-sized Al 2 O 3 particles on the microstructure and properties of copper matrix was the object of this study. The mixture of inert gas-atomized prealloyed copper powder (with 1 wt.% Al) and 0.6 wt.% commercial Al 2 O 3 powder (serving as micro-sized particles) was used as the starting materials. Strengthening of the copper matrix was performed by treating the powders in the air for up to 20 h in the planetary ball mill. During milling of the prealloyed powder, finely dispersed nano-sized Al 2 O 3 particles were formed in situ by internal oxidation. The approximate size of these particles was between 30 and 60 nm. The highest values of microhardness were reached in compacts processed from 10 h-milled powders. The microhardness of compact obtained from 10 h-milled powder was 3 times higher than the microhardness of compact processed from as-received and non-milled prealloyed powder. At the maximum microhardness the grain size reaches the smallest value as a result of the synergetic effect of nano- and micro-sized Al 2 O 3 particles. Recrystallization, which occurred during prolonged milling, was the main factor influencing the decrease in microhardness. The increase in electrical conductivity of compacts after 15 h of milling is the result of the decrease in microhardness and activated recrystallization processes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.