Abstract
Myristic acid-palmitic acid-tetradecanol/expanded graphite (MA-PA-TD/EG) and myristic acid-stearic acid-lauric acid/ expanded graphite (MA-SA-LA/EG) were obtained. MA-PA-TD/EG and MA-SA-LA/EG for the optimum mass ratio of 8:1 were investigated by DSC, FT-IR, TG, and SEM, and it was shown that MA-PA-TD and MA-SA-LA phase change materials were evenly distributed in expanded graphite through capillary force. Phase transition temperatures of MA-PA-TD/EG and MA-SA-LA/EG before and after cooling and heating cycles were 34.14, 34.39 °C and 30.21, 30.33 °C, respectively, and MA-PA-TD/EG and MA-SA-LA/EG had good stability. On the other hand, MA-PA-TD/EG was 67% faster than that of MA-PA-TD during solid–liquid phase change, and MA-SA-LA/EG was 63% faster than that of MA-SA-LA. Meanwhile, MA-PA-TD/EG and MA-SA-LA/EG had good thermal stability and heat storage according to thermogravimetric experiments. Therefore, MA-PA-TD/EG and MA-SA-LA/EG are suitable for practical application in buildings.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.