Abstract
The process characteristics of the synergic cold metal transfer (CMT) process have been examined for welding aluminium alloy. Utilising a simple backlighting system and through the arc monitoring the droplet transfer modes were identified. Whilst the modified short circuit mode was evident for the lower parameter range, a two part transfer mode based upon a combination of spray and short circuit transfer was observed for the mid to upper parameter range. The technology was also explored as a cladding process for applying to ternary alloyed (Al–Cu–Mg) aluminium plate. This alloy system is known to be susceptible to solidification cracking when MIG welded using the binary Al-2319 (Al–Cu) filler wire, this being due to the wide element freezing range of the weld resulting from mixing with the base material. Utilising this filler, weld dilution ratios for both CMT and pulsed welding were identified across the examined parameter range. The CMT process exhibited greater control of dilution that enabled deposition of a quasi-binary (Al–Cu) layer exhibiting a less crack susceptible composition. Onto this layer conventional MIG welding could be applied which could potentially eradicate cracking using a binary filler wire.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.