Abstract
ABSTRACTThe aim of this work is to investigate the effects of different stretching processes on breathability performance of linear low‐density polyethylene (LLDPE)/coated calcium carbonate (CaCO3) composite films under the same conditions. Coated calcium carbonates and powdered LLDPE were physically mixed and dried in a high shear mixer, and polymer compounds containing 45 and 55 wt% coated calcium carbonate were generated using a twin screw extruder. Cast films were produced and then they were stretched 3.5 times in machine direction at 25°C by using stenter and interdigitation stretching methods. It was revealed that not only the CaCO3 type and loading amount but also the stretching type has an enormous effect on breathability performance. In addition, the quality of porosity, that is, the amount of interconnecting pores, was determined to play an important role in breathability. And, the interdigitation stretching process offers the potential for a better breathability at reduced processing costs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.