Changes in X-ray photoelectron spectra of yttria-tetragonal zirconia polycrystal by ion sputtering

Abstract

This paper reports changes in X-ray photoelectron spectroscopy spectra of yttria-tetragonal zirconia polycrystal (Y-TZP) brought about by Ar ion sputtering. The changes in the core-level spectra of Y-TZP suggest that preferential sputtering of oxygen occurred. A new peak was observed near 0 eV binding energy accompanied with changes in the core-level spectra by the sputtering. After 18 h in a high vacuum following the sputtering, the spectra changed by the sputtering were returned to their original shapes. In contrast, the color of Y-TZP was changed from white to pale brown by X-ray irradiation and was changed from pale brown to dark gray by ion sputtering. However, when the new peak near 0 eV decreased after 18 h, no color change was observed. Therefore, it is thought that the new peak was mainly derived from electrons trapped in various kinds of oxygen vacancies created by the sputtering in other than color centers.