Abstract
The substitution of Lanthanum into barium hexaferrite (Ba1-xLaxFe12O19) for La3+ (x = 0, 0.2, 0.4, and 0.6) has been synthesized using the solid reaction method through mechanical milling. Refinement results from X-ray diffraction patterns (XRD) showed that the formation of hexagonal crystal structures with space group P63/mmc, where the lattice parameters of a = b and c decreased, while the lattice strain obtained increased with increasing La concentration in the sample. The single phase is obtained at the concentration of x = 0, while the concentration of x = 0.2, 0.4 and 0.6 are already multi-phase. The morphological observation of particles using a scanning electron microscope (SEM) shows that with the presence of the La3+ substitution results the particle size distribution varies. Saturation magnetization and magnetocrystalline anisotropy are reduced due to this La substitution. This is thought to be caused by a decrease in magnetic (Fe-O-Fe) interaction and a reduction in the barium hexaferrite phase fraction in the sample. It was concluded that the effect of La substitution on Ba1-xLaxFe12O19 resulted in changes in Crystal structure parameters, particle size distribution, and magnetic properties of the material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.