Abstract
Artificial graphite is typically manufactured by carbonization of a shaped body of a kneaded mixture using granular cokes as a filler and pitch as a binder. It undergoes a pitch impregnation process if necessary and finally applying graphitization heat treatment. The effect of thermal oxidation in air or a CO 2 atmosphere on IG-11 graphite samples is investigated in this study. The results show a localized oxidation process that progressively reveals the large coke particles with increasing level of overall weight loss in air. The surface of the graphite was peeled off and no change was found in the specific gravity after air oxidation. However, the specific gravity of graphite was continuously decreased by CO 2 oxidation. The decrease in the specific gravity by CO 2 oxidation was due to CO 2 gas that progressed from the surface to the interior. The pore shape after CO 2 oxidation differed from that under air oxidation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.