Abstract
Electrochemical material characterization method was applied to the creep specimens of 12%Cr ferritic steel to evaluate the changes in precipitates during creep. Experimental results revealed that the peak current densities “Ip1” and “Ip2” appeared at specific potentials during anodic polarization curve measurement in 1M-KOH solution. These peak current densities corresponded to the selective dissolution of several kinds of precipitates, respectively. The Ip2, which reflected the amount of M23C6 and Laves phase, increased more siginificantly with creep than thermal aging. On the other hand, the effect of applied stress was not reflected on the change in Ip1, although it increased with thermal aging and creep as well as the Ip2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.