Abstract
Co48-xFexCr15Mo14C15B6Er2 (x = 2.5 and 5) bulk metallic glasses (BMGs) with critical size (dc) up to 15 mm in diameter were synthesized by copper mold casting. Co43Fe5Cr15Mo14C15B6Er2 BMG has a wide supercooled liquid region (84 K) and ultrahigh fracture strength exceeding 5000 MPa, which is the highest value for reported metallic glasses with dc exceeding 1 cm. Furthermore, the Poisson ratio, Young modulus, shear modulus and bulk modulus of this alloy were evaluated to be 0.31, 217 GPa, 82 GPa and 214 GPa, respectively. The ideal configurational entropy of Co48−xFexCr15Mo14C15B6Er2 (x = 0 and 5) has been calculated. The introduction of the similar element Fe in the Fe-free Co-Cr-Mo-C-B-Er alloy will be beneficial to increasing the ideal configurational entropy and depressing the critical cooling rate to achieve greater glass-forming ability. The combination of superior glass-forming ability and ultrahigh fracture strength makes the present Co48-xFexCr15Mo14C15B6Er2 (x = 2.5 and 5) BMGs promising candidates as advanced structural materials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.