Cement and Clinker Production by Indirect Mechanosynthesis Process

Abstract

Global cement production has reached 3.9 billion tons. However, the clinkerization process, which is the basis of cement production, is responsible for an approximate annual global CO2 emission of 2 billion tons. As part of CEMBUREAU’s 5C strategy, the European cement industry aims to achieve carbon neutrality throughout the cement-concrete value chain by 2050. This article is a continuation of the previous article on the indirect mechanosynthesis clinkerization process, which combines mechanical activation (high-energy milling) and thermal treatment at lower temperatures (from 900 °C) than those used for conventional clinkerization to produce clinker. With this process, we manufactured cement and clinker from industrial and laboratory raw mixes, which had to be rectified by adding kaolinite in compliance with the different cement indicators (LSF, SM, AM). The cement and clinker produced by indirect mechanosynthesis (15 min of mechanical activation and heat treatment 900 °C or 1200 °C) were characterized. In order to test the hydraulic properties of the cement produced, cement pastes were made. Mechanical and structural studies were carried out (between 70 and 90% of C2S). Mechanical tests revealed for 7 curing days, the values of 3.60 and 7.60 MPa at 900 °C and 1200 °C, respectively, in comparison to commercial cements CEM I and CEM III (23.03 and 19.14 MPa).