Cell Wall Property Changes of White Rot Larch during Decay Process

Abstract

Larch flakes infested with white rot fungus were examined following several infestation durations with respect to the mass loss, tensile strength, hardness, porosity, and change in cell wall components. Nano-indentation, X-ray diffraction (XRD), nitrogen adsorption, and Fourier transform infrared (FTIR) spectroscopy testing methods were employed to investigate the property changes during the decay process. The testing results showed that the mass loss was greater and the longitudinal tensile strength decreased following the first three-week infestation. Nano-indentation measurements revealed that the average MOE of infested larch flakes decreased from 24.0 to 17.1 GPa and the average hardness declined from 528.47 to 427.87 MPa following 12 weeks of infestation. After the first three weeks, the relative crystallinity, surface area, and micropore area of the infested samples increased. These parameters decreased after three weeks had elapsed. Changes in the absorption peaks observed in FTIR explained that the first three-week infestation had a strong effect on the mass loss and strength changes. This suggests that white rot fungus intensely attacked the lignin component of the biomass during the first three weeks of infestation.