Abstract
The cavitation erosion behavior of Hastelloy C-276 alloy was investigated using an ultrasonic vibratory apparatus and compared with that of 316L stainless steel. The mean depth of erosion (MDE) and erosion rate (ER) curves vs. test time were attained for Hastelloy C-276 alloy. Morphology and microstructure evolution of the eroded surface were observed by scanning electron microscopy (SEM) and field emission scanning electron microscopy (FESEM) and the predominant erosion mechanism was also discussed. The results show that the MDE is about 1/6 times lower than that of the stainless steel after 9h of testing. The incubation period of Hastelloy C-276 alloy is about 3 times longer than that of 316L stainless steel. The cavitation-induced nanometer-scaled precipitates were found in the local zones of the eroded surface for Hastelloy C-276. The selective cavitation erosion was found in Hastelloy C-276 alloy. The formation of nanometer-scaled precipitates in the eroded surface may play a significant role in the cavitation erosion resistance of Hastelloy C-276.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.