Abstract
Epoxy/polycaprolactone (PCL) blends containing cationic photo-initiator were prepared by both solution and melt blending. These materials were processed by solvent casting, solution electrospinning (SE), melt electrowriting (MEW), and Fused Deposition Modeling (FDM) 3D printing. The final materials were obtained after UV curing at room temperature. FTIR, and gel content measurements showed that all the materials were crosslinked and that the PCL was part of the network. The shape memory abilities (measured by DMA experiments) depended on the processing technique. Thus, the fixity and recovery ratios were optimal for electrospun fibers, while the 3D printed sample was not able to recover any shape, probably because of the poor adhesion between the printed layers. According to AFM images, samples obtained by MEW and 3D printing produced materials with spherulitic morphology, while solution electrospinning rendered fibers with Shish-Kebab-type crystalline morphology. The latter was highly anisotropic, and many chains were oriented along the nanofiber axis interdispersed with amorphous regions where the epoxy resin formed covalent links with the PCL chains. This morphology conferred extraordinary solvent resistance and shape memory properties to the electrospun mats. The latter manifested a very high affinity towards chloroform, and accordingly, they displayed potential applications as chloroform sensors.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.