Abstract
The method of neutron diffraction coupled with isotopic substitution is presented and recent investigations on the environment around cations in silicate (Ti in K 2O·TiO 2·2SiO 2, Ca and Ni in 2CaO·NiO·3SiO 2) and aluminosilicate (Li in Li 2O·Al 2O 3·2SiO 2) glasses are reviewed. The examination of the cation-centered pairs obtained from the first difference function presents striking similarities for all investigated cations. These functions indicate a well-defined short- and medium-range environment around cations. The local site generally presents a lower coordination number than that found in the crystals of similar composition. The environment around Ti in vitreous K 2O·TiO 2·2SiO 2 corresponds to a square-based pyramid and direct TiO 5–TiO 5 linkages were observed experimentally in the second difference function, contrary to crystals. A detailed description of the cation site distortion for Li and Ca may be given by this method. The distribution of cations at medium range, which can be extracted by the double difference method, reveals the presence of cation-rich regions in silicate glasses. The cation–cation distances often indicate a two-dimensional character in the cationic organization. On the contrary, Li-aluminosilicate glass shows a more homogeneous cation distribution, in relation with the charge-compensating role of Li in this glass. This non-homogeneous distribution of cations may be related to the nano-inhomogeneities proposed in the models of supercooled liquids.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.