Abstract
AbstractA sample of ferripyrophyllite, a mineral with ideal composition Fe2SiO10(OH)2, was analyzed by Mössbauer spectroscopy, magnetization and magnetic susceptibility measurements. The iron is entirely ferric, and the main feature of the Mössbauer spectrum at room temperature is a single absorption line with isomer shift δ = 0.36(1) mm/sec due to iron in M2 sites. The line is broadened by a slight quadrupole splitting Δ = 0.18(1) mm/sec, the smallest yet reported for a sheet silicate. Weaker features corresponding to quadrupole doublets with relative intensities of 7% and 8% having δ = 0.43(1) mm/sec; Δ = 1.22(2) mm/sec and δ = 0.14(1) mm/sec; Δ = 0.59(2) mm/sec are assigned to ferric iron in nonequivalent octahedral and tetrahedral sites, respectively, giving the following formula, based on published chemical analysis: Ca0.05(Fe3+1.87Mg0.11Al0.09)VI(Si3.80Fe3+0.16Al0.04)IVO10(OH)2, where Ca is in interlayer sites. Ferripyrophyllite orders antiferromagnetically at 18(2)°K. The Mössbauer spectrum at 4.2°K consists of a single, resolved magnetic pattern with hyperfine field Bhf = 51.8 T. The relatively high Néel temperature compared with other dioctahedral ferric phyllosilicates provides further evidence that Fe3+ cations tend to be ordered on M2 sites within the octahedral sheet.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.