Abstract
Combinational studies of synchrotron X-rays and neutrons have been performed to determine the site occupancy, valence state and magnetic structure of M-type BaTiMnFe10O19. X-ray resonant scattering studies have revealed the site preference, where Ti and Mn ions are distributed evenly over the Fe1, Fe2 and Fe3 sites of five independent Fe sites. X-ray absorption near-edge structure (XANES) and X-ray magnetic circular dichroism (XMCD) results for BaTiMnFe10O19 are similar to those of BaFe12O19 at the Fe K absorption edge. Clear chemical shifts exist at both the Mn and Fe edges, suggestive of a mixed valence of Mn and Fe ions. The Mn K XANES resembles Mn–Zn ferrite, where the observed fourfold peak is explained as the presence of four-coordinated Mn ions, on the basis of the self-consistent calculation of relativistic density functional theory. This can be explained by the presence of spinel substructures within the S block layer. Satellite reflections of 002 ± τ and 004 − τ (τ = 2/3) on 00l were observed at a temperature of 8 K in neutron powder diffraction, due to magnetic scattering on the helicoidal arrangement of ordered spins with a propagation period of c/τ. The magnetic structure observed in the neutron powder diffraction and the XMCD results explain the decreasing uniaxial magnetization from BaFe12O19.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.