Catalytic pyrolysis of ulva lactuca macroalgae: Effects of mono and bimetallic catalysts and reaction parameters on bio-oil up-gradation

Abstract

Catalytic pyrolysis of ulva lactuca (UL) macroalgae was studied over a series of ZrO2 supported metal such as Co, Ni and Co-Ni metal catalysts at temperature range of 300–500 °C. Highest bio-oil yield (47.8 wt%) was found with Co-Ni/ZrO2 (10 wt%) catalyst while non-catalytic yielded 42.5 wt% bio-oil. Moreover with increases the metal amount to 15 wt%, the bio-oil yield slightly increased (49.2 wt%). The bio-oil quality significantly improved with using the catalysts compared to the non-catalytic pyrolysis. Catalytic pyrolysis also revealed that introducing Co-Ni into the ZrO2 could result in higher surface area and which increased active sites. Catalytic bio-oils were consisted of mainly long chain hydrocarbon in the range of C6-C16. Moreover, the catalytic bio-oils were showed the higher ‘high heating value’ (HHV) 38.1 MJ/kg as compare to non-catalytic bio-oils (29.4 MJ/kg). Catalysts have been showed excellent recyclability on bio-oil yield and compounds selectivity.