Reforming of toluene with model exhaust gas was carried out as Reformed EGR of gasoline engine mainly at 773 K with Ni-M/Mg/Al (Ni 12 wt%, M = Fe, Co, Cu) prepared from corresponding hydrotalcite-like compounds. Ni-Fe/Mg/Al (Fe/Ni = 0.1–0.5) showed clearly higher performance than Ni/Mg/Al in terms of activity, coke-deposition resistance and stability. In contrast, Ni-M/Mg/Al (M/Ni = 0.25, M = Co, Cu) showed similar behaviors to Ni/Mg/Al. The optimum Fe/Ni ratio was 0.25 from toluene conversion and the suppression of benzene formation. Ni-Fe/Mg/Al (Fe/Ni = 0.25) showed high coke-deposition resistance at any position of the catalyst bed, indicating that both substrate decomposition and CO disproportionation were suppressed. The coke amount was not increased even at low temperature (773 K) or higher toluene partial pressure (toluene/H2O/N2/CO2 = 0.5–1.2/11.8/71.2/11.8, molar ratio), but the activity gradually decreased under such conditions. The Ni-Fe alloy nanoparticles in the reduced Ni-Fe/Mg/Al were almost unchanged during the reaction. The deactivated catalyst was regenerated successfully by the treatment under N2 at 873 K, catalytic use at 973 K or re-reduction. These results suggest that the deactivation was caused by carbonaceous species which can be removed easily even by N2 treatment, rather than by graphite-like coke that is difficult to be eliminated via such simple treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.