Catalyst-Free Direct Vapor-Phase Growth of Hexagonal ZnO Nanowires on α-Al2O3

Abstract

The evolution of ZnO nanowires has been studied under supersaturation of Zn metal species with and without a ZnO thin-film buffer layer on α-Al2O3 deposited by the pulsed laser ablation technique. The nanowires had diameters in the range of 30 nm to 50 nm and lengths in the range of 5 μm to 10 μm with clear hexagonal shape and \( [000\bar{1}] \), \( [10\bar{1}1] \), and \( [10\bar{1}0] \) facets. X-ray diffraction (XRD) measurements indicated crystalline properties for the ZnO nanostructures grown on pulsed laser deposition (PLD) ZnO nucleation layers. The optical properties were analyzed by photoluminescence (PL) and cathodoluminescence (CL) measurements. The ZnO nanowires were found to emit strong ultraviolet (UV) light at 386 nm and weak green emission as observed by PL measurements. The stoichiometry of Zn and O was found to be close to 1 by x-ray photoelectron spectroscopy (XPS) measurements. The process-dependent growth properties of ZnO nanostructures can be harnessed for future development of nanoelectronic components including optically pumped lasers, optical modulators, detectors, electron emitters, and gas sensors.