Abstract
Corrosion of structural alloys in fluoride salt cooled high temperature reactors (FHRs) is affected by the presence of carbon. The stability of the carbides of alloying elements augments their corrosion, however the same property can be useful if these stable carbides are used to protect materials. Exposure tests of pure elements Cr, Fe, Ni, W, and Mo in graphite crucibles at 700 °C were conducted in molten FLiNaK salt for 100 h. Carbide particles were detected on the surfaces of Cr, Mo, and W samples after exposure. The ranking of these elements, from least to greatest corrosion resistance by mass loss per unit area was Cr < Fe < W < Mo < Ni. The stability of chromium carbides was further investigated using chromium samples which were pre-carburized in a reducing hydrocarbon environment at 800 °C prior to exposure tests in molten FLiNaK. The chromium carbide layer produced by pre-carburization was resistant to attack by molten fluoride and slowed corrosion of the underlying chromium metal.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.