Abstract
PtRu/C catalyst is synthesized by microwave-assisted polyol process. Then, the PtRu nanoparticles are riveted through glucose in-situ carbonization by hydrothermal method. X-ray diffraction, transmission electron microscopy, cyclic voltammograms, COad stripping voltammetry, electrochemical impedance spectroscopy and accelerated potential cycling tests have been carried out to characterize their properties. The experimental results indicate that the average sizes of PtRu nanoparticles grow up from 1.54 nm to 2.56 nm after hydrothermal method. The electrochemical active specific surface areas of as-prepared and carbon riveted PtRu/C are 73.0 m2 g−1 Pt and 89.6 m2 g−1 Pt, respectively. The durability of carbon riveted PtRu/C increases one time after APCT of 1000 cycles and its mass activity also enhances 6% in first cycles in comparison with that of as-prepared PtRu/C. An enhanced stability of carbon riveted PtRu/C is mainly attributed to the existence of carbon nanolayer on the surface of the support from glucose in-situ carbonization to inhibit the migration and coalescence of PtRu nanoparticles on the support during work. Besides, the increased ratio of Pt(0), Ru(0), and carbon groups with higher stability and the evidently decreased of PtO2 and RuOxHy on surface of carbon riveted PtRu/C is another important reason to enhance its durability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.