Abstract
Nanoparticles of CaSO4 : Dy phosphor with a particle size of around 30 nm have been prepared by the chemical co-precipitation technique. Pellet samples of the nanomaterials were irradiated by a 75 MeV C6+ ion beam at the fluence range 1 × 109–1 × 1013 ions cm−2. Thermoluminescence (TL) glow curves of the irradiated samples were recorded and studied. The microcrystalline form of this sample is also included in the study with the aim of reporting a comparative measurement. The TL analysis shows that the glow curve of the nanomaterial has two peaks at around 166 and 210 °C. These peaks are similar to those induced in the microcrystalline sample with a slight difference in their TL response. The second peak is more prominent in the case of the microcrystalline sample at low fluences, while the first one dominates in the nanostructured sample mainly at higher fluences. The TRIM code based on Monte Carlo simulation was also used for calculating some ion beam parameters. Dosimetric properties of the carbon ion beam irradiated materials show that the nanostructure material has excellent features such as a simple glow curve structure and a linear TL response over a wider range than the corresponding microcrystalline sample. These results show that the nanostructure form of CaSO4 : Dy might be useful for detecting the high doses of carbon ions used in radiotherapy. Thermal analysis of the prepared nano- and microcrystalline materials was also done in the range 50–500 °C using thermogravimetry analysis and differential thermal analysis. No phase transitions within this range of heating for both the materials are observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have