Abstract
Tradeoff limitation on selectivity and permeability restricts the use of membranes for CO2 separation in natural gas industry. Mixed matrix membranes (MMMs) with combined advantages of polymeric matrix and inorganic fillers have been long proposed to overcome this shortcoming, but thick dense symmetric layer structure with a high mass resistance offers improvement in selectivity only. In this study, asymmetric polysulfone MMMs incorporated with small pore zeolite were proposed. SAPO-34 zeolite with a framework of 0.38nm pore size and high CO2 adsorption affinity was used as inorganic fillers. The asymmetric mixed matrix membrane structure was prepared using the phase inversion method. The effects of zeolite loading (5–30wt.%) on the membrane characteristics were studied using SEM with EDX, FT-IR, and TGA; while the gas transport properties were investigated using pure gas permeation tests of N2, CO2 and CH4. Well dispersion of SAPO-34 particles in the polymer matrix was observed for zeolite loading less than 10wt.%. The maximum CO2 permeance (314.02GPU) was achieved by incorporating 10wt.% of SAPO-34 into asymmetric PSf membrane. Even without strong binding between PSf and SAPO-34, CO2/N2 and CO2/CH4 selectivities up to 26.1 and 28.2 respectively were observed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.