Abstract
This study aimed to compare in vivo osteogenesis on rough threaded dental implants with and without calcium phosphate (CaP) coating deposition, alone or in association with low-level laser therapy (LLLT) by gallium aluminum arsenide. Four groups were studied: G1: implant; G2: implant + CaP coating; G3: implant + LLLT; and G4: implant + CaP coating + LLLT. LLLT was applied for 7 days at the surgical site before and after placing the implant. Topographic characterization was performed before surgery using scanning electron microscopy and energy dispersion spectrophotometry. Bone-implant contact (BIC) was measured after 1, 2, and 6 weeks and reverse torque after 6 weeks. In short periods, G2, G3, and G4 showed significantly greater BIC than G1 (P < 0.05), but no difference in BIC was observed at 6 weeks. However, the values for the removal torque test at 6 weeks were higher in G2 and G4 (P < 0.05). Both CaP coating alone and using LLLT induce cellular stimulation and improve BIC in short-term healing, resulting in higher implant fixation, and should be considered in clinical practice due to their low cost and high effectiveness.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.