Abstract
The low oxidation resistance of SiMo ductile cast irons used as exhaust manifold material at high temperatures necessitates the development of new generation ductile cast iron compositions. New alloy designs can be made using CALPHAD methodology, and solidification sequence, segregation and critical phase transformation temperatures can be determined, especially for the solidified bulk materials. Thus, in commercial practicality, castable compositions with a raised A1 temperature can be obtained. In this study, novel SiNb cast irons with varying silicon contents were developed as candidate materials for exhaust manifolds. Solidification sequence, microsegregation, phase transformations, equilibrium phases of hypereutectic compositions containing 4 to 7 wt pct Si were calculated by CALPHAD-based modeling. The bulk materials of the studied compositions were cast as Y blocks and metallurgical analyzes were carried out. Studies revealed that; (i) in the ferritic matrix of the cast irons, graphite, Nb-rich carbides and some pearlite existed, (ii) pearlite formation was due to the negative segregation of silicon and positive segregation of manganese during solidification, (iii) as silicon content increased the amount of silicon dissolved in ferrite phase increased in the solidified structure and as a result pearlite formation decreased at the cell boundaries, and amount of vermicular graphite increased, (iv) depending on the silicon content the critical A1 temperature varied between 860 °C to 1013 °C and these values were higher than that of SiMo cast iron. All these findings revealed that SiNb cast irons had phase stability at higher temperatures compared to SiMo cast iron.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.