Abstract
Specific heat spectroscopy in the frequency range from 1 Hz to 103 Hz with a sensitivity of pJ K−1 was employed to study the glass transition behavior of ultrathin poly(bisphenol A carbonate) (PBAC) films with thicknesses ranging from 192 nm down to 10 nm. The amplitude and the phase angle of the complex differential voltage as a measure of the complex heat capacity were obtained as a function of temperature at a given frequency simultaneously. Both spectra are used to determine the dynamic glass transition temperature as a function of both the frequency and the film thickness. As the main result no thickness dependence of the dynamic glass transition temperature was observed down to a film thickness of 10 nm within the experimental uncertainty of ±3 K. The obtained data were compared with literature results in detail.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.