Abstract
Calcium phosphate coatings are known to enhance long-term fixation, reliability and promote osteointegration of cementless titanium-based implant devices. This study was aimed at the pulsed laser deposition of calcium phosphate coatings onto titanium using hydroxyapatite and hydroxyapatite–fluorapatite targets. The deposition was carried out at the high laser beam fluence conditions, about 12 J/cm 2. The coatings were characterized with respect to their morphology, phase composition and hardness. X-ray energy dispersive analysis revealed the coatings retain their elemental composition, and fluoride content within the film is the same as in the initial target. However, unlike sintered targets, the deposited films contain no apatite-like phases. The hardness of the films, about 18 GPa, is surprisingly high compared to that of hydroxyapatite and hydroxyapatite–fluorapatite ceramic targets. The deposited coatings of 2.7–2.9 μm thickness have uniform and dense microstructure, containing the solidified droplets of the expulsed from the target phase. The uncommon structure and hardness of the films can be attributed to the melting and phase decomposition of the initial material in the laser plasma.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callSimilar Papers
More From: Biomaterials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.