Abstract
ABSTRACT The main chemical components of waste cow bones are apatite minerals, especially those containing calcium and phosphorus. This study investigated whether this bone could produce extracted hydroxyapatite through calcining at 900° C for different holding times (1–6 h). An average mass loss of 45% occurred in this experiment during the preparation of bone powders, which involved crushing and further calcining at this temperature. The quantitative XRD analysis showed that 99.97 wt.% hydroxyapatite and over 0.3 wt.% calcite were present in the raw and as-calcined bone powders, with trace amounts of CaFe3O5 (calcium ferrite) phases appearing in the calcined product. Depending on the holding calcining times, SEM images of the calcined bovine powders revealed aggregate sizes ranging from 0.5–3 µm and crystallite (grain) sizes ranging from 70 to 340 nm in all calcium-phosphate powder products. Following EDX analysis of all sample surfaces, possible calcium-deficient hydroxyapatite instead of hydroxyapatite formed, as evidenced by the calcined product's Ca/P ratio exceeding 1.67. Additionally, calcining cow bones for 5–6 h at 900° C yielded a high-purity nano-crystalline hydroxyapatite powder precursor in biomedical applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.