BWR pipe crack and weld clad overlay studies

Abstract

Several topics pertaining to the problem of stress corrosion cracking (SCC) of piping in boiling water reactors are addressed in this paper: (1) the effects of impurities, dissolved oxygen content, and strain rate on susceptibility of SCC of “Nuclear Grade” Type 316NG and sensitized Type 304 stainless steel, (2) finite-element analyses and experimental measurement of residual stresses in weldments with weld overlays, and (3) analysis of field components to assess effectiveness of in-service inspection techniques and the in-reactor performance of weld overlays. Several anion impurities including sulfates, chlorides, nitrates, borates, and carbonates were studied under both near neutral and slightly acidic conditions. At the low impurity concentrations expected in reactor coolant systems (<0.1 ppm), the sulfur species appear to be the most deleterious. They promote intergranular SCC in sensitized stainless steel and transgranular SCC in the low-carbon “Nuclear Grade” stainless steel. Correlations between experimental data and a phenomenological model that describes the effect of strain rate on SCC are presented. Measurements of the residual stresses produced by weld overlays confirm that the process is very effective in producing compressive stresses on the inner surface of the weldment. Examination of a weld overlay removed from service suggests that no additional throughwall crack growth had occurred after application of the overlay.