Abstract
Spinel ferrite NiFe2 O4 thin films have been grown on three isostructural substrates, MgAl2 O4 , MgGa2 O4 , and CoGa2 O4 using pulsed laser deposition. These substrates have lattice mismatches of 3.1%, 0.8%, and 0.2%, respectively, with NiFe2 O4 . As expected, the films grown on MgAl2 O4 substrate show the presence of the antiphase boundary defects. However, no antiphase boundaries (APBs) are observed for films grown on near-lattice-matched substrates MgGa2 O4 and CoGa2 O4 . This demonstrates that by using isostructural and lattice-matched substrates, the formation of APBs can be avoided in NiFe2 O4 thin films. Consequently, static and dynamic magnetic properties comparable with the bulk can be realized. Initial results indicate similar improvements in film quality and magnetic properties due to the elimination of APBs in other members of the spinel ferrite family, such as Fe3 O4 and CoFe2 O4 , which have similar crystallographic structure and lattice constants as NiFe2 O4 .
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.