Abstract

The fabrication of silicon based micromechanical sensors often requires bulk silicon etching after aluminum metallization. All wet silicon etchants including ordinary undoped tetramethyl ammonium hydroxide (TMAH)–water solution attack the overlaying aluminum metal interconnect during the anisotropic etching of (100) silicon. This paper presents a TMAH–water based etching recipe to achieve high silicon etch rate, a smooth etched surface and almost total protection of the exposed aluminum metallization. The etch rate measurements of (100) silicon, silicon dioxide and aluminum along with the morphology studies of etched surfaces are performed on both n-type and p-type silicon wafers at different concentrations (2, 5, 10 and 15%) for undoped TMAH treated at various temperatures as well as for TMAH solution doped separately and simultaneously with silicic acid and ammonium peroxodisulphate (AP). It is established through a detailed study that 5% TMAH–water solution dual doped with 38 gm/l silicic acid and 7 gm/l AP yields a reasonably high (100) silicon etch rate of 70 μm/h at 80 °C, very small etch rates of SiO 2 and pure aluminum (around 80 Å/h and 50 Å/h, respectively), and a smooth surface (±7 nm) at a bath temperature of 80 °C. The etchant has been successfully used for fabricating several MEMS structures like piezoresistive accelerometer, vaporizing liquid micro-thruster and flow sensor. In all cases, the bulk micromachining is carried out after the formation of aluminum interconnects which is found to remain unaffected during the prolonged etching process at 80 °C. The TMAH based etchant may be attractive in industry due to its compatibility with standard CMOS process.

Full Text
Published version (Free)

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call