Abstract
Organic-inorganic hybrid perovskites have aroused intense research interest because of their excellent physical performance and potential for use in optoelectronic field. Herein, we report two new 2D hybrid lead bromides, (C7H18N2)PbBr4 [C7H18N2 is 1,7-diaminoheptane] and (C9H22N2)PbBr4 [C9H22N2 is 1,9-diaminononane], both of which possess ⟨100⟩-oriented inorganic layers consisting of corner-sharing octahedra. The optical bandgaps are experimentally determined to be 2.76 eV for (C7H18N2)PbBr4 and 2.78 eV for (C9H22N2)PbBr4. Upon 390 nm excitation, (C7H18N2)PbBr4 exhibits white-light emission centered at 600 nm, and (C9H22N2)PbBr4 exhibits red-light emission centered at 620 nm. These broad photoluminescent spectra originate from the synergistic emission of free excitons (FEs) and self-trapped excitons (STEs). This work provides a strategy for realizing single-component white-light emission and efficient red-light emission in two-dimensional perovskites, demonstrating the vast application prospects of 2D perovskites in photoelectric devices.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.