Bright, small sizes and hydro-dispersive NIR persistent luminescence nanoparticles modified with Si and amino groups for enhanced bioimaging

Abstract

Near-infrared (NIR) persistent luminescence nanoparticles (PLNPs) with high brightness, small sizes, good hydro-dispersivity, and intrinsic surface-functional groups are desirable in biological applications. In this work, Cr3+-doped zinc gallogermanates Zn1+x Ga2−2x Ge x O4:Cr (ZGGC) PLNPs were hydrothermally synthesized via 3-aminopropyltriethoxysilane (APTES) as an additive, or APTES and cetyltrimethylammonium bromide (CTAB) as two co-additives. Addition of APTES not only dramatically enhances the 696 nm NIR luminescence intensity, but also obviously decreases the particle size and introduces amino groups. In particular, the x = 0.1 series ZGGC (ZGGC0.1) with the addition of n moles equivalent APTES (ZGGC0.1-nA) had smaller particle sizes than the x = 0.2 counterpart (ZGGC0.2-nA). The NIR afterglow intensities increased with the APTES introduction. The ZGGC0.2-2.5A sample (also named as ZGGC, Si, -NH2) exhibited maximum luminescence intensities both in solid and aqueous states. With APTES, Si atom is doped and –NH2 groups are modified, the trap depth and density become larger, and the afterglow intensities and decay time are significantly enhanced. More notably, co-addition of CTAB (ZGGC0.2-2.5A-C) (also named as ZGGC, Si, −NH2’) further enhances hydro-dispersivity and luminescence intensity, decreases particle sizes, and results in more prominent amino groups. The trap density is drastically higher than that without CTAB (i.e. ZGGC0.2-2.5A). Change of Cr3+ microenvironment in the crystal and more defects introduction contribute to the enhanced brightness. As expected, the ZGGC,Si,-NH2’ PLNPs possess excellent biocompatibility, deep tissue penetration and distinguished bioimaging properties, and rechargeability with orange LED light. The ZGGC,Si,-NH2’ PLNPs should provide to be an excellent nanomaterial for various functionalization and bioimaging applications.