Branched polyisoprene (PI) was prepared from PI-macromonomers. Linear byproducts of the synthesized polymer were removed by means of inverse spin fractionation, using the solvent cyclohexane (CH) and the precipitant acetone (AC). A well-defined fraction (Mw = 17.5 kg/mol, Mw/Mn = 1.8) of the branched polyisoprene obtained in this manner was used to determine different phase diagrams with branched and/or linear PI in the mixed solvent CH/AC at 25 °C. For comparable molar masses of the polymers the two-phase area is smallest for the branched PI and slightly larger for the linear PI; in the case of the unfractionated original sample of the branched polymer one observes a pronounced peninsula of immiscibility extending into the region of high CH concentrations. This feature is attributed to a large miscibility gap between the branched and the linear polymer, which was studied in more detail for the ternary system CH/branched PI/linear PI.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.