Abstract
Branched MnOOH nanorods with diameters in the range of 50-150 nm and lengths of up to tens of micrometers were prepared by using potassium permanganate (KMnO(4)) and PEG 400 (PEG=polyethylene glycol) as starting materials through a simple hydrothermal process at 160 °C. After annealing at 300 °C under a N(2) atmosphere for 5 h, MnOOH nanorods became gradually dehydrated and transformed into mesoporous Mn(3)O(4) nanorods with a slight size-shrinking. The as-obtained mesoporous Mn(3)O(4) nanorods had an average surface area of 32.88 m(2) g(-1) and a mean pore size of 3.7 nm. Through tuning the experimental parameters, such as the annealing atmosphere and temperature, β-MnO(2), Mn(2)O(3), Mn(3)O(4), MnO, and Mn(5)O(8) were selectively produced. Among these structures, mesoporous Mn(3)O(4) nanorods were efficient for the catalytic degradation of methylene blue (MB) in the presence of H(2)O(2) at 80 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.