Borosilicate glass as a surface finishing alternative for improving the mechanical properties of third-generation zirconia

Abstract

ObjectiveThis study evaluated the effect of an experimental borosilicate glass on the mechanical and optical behavior of 5Y-PSZ zirconia and comparing it to commercial glaze and as-sintered. MethodsDisc-shaped specimens of a 5Y-PSZ (Zpex Smile) were prepared and sintered (1550 °C, 2 h). The zirconia discs were randomly divided according to the surface treatment: as-sintered (C), commercial glaze (G), and experimental borosilicate glass (SL). Glaze and experimental glass powders were mixed with building liquids and applied to zirconia with a brush. G specimens were fired at 950 °C and SL at 1200 °C. An extended dwell time of 20 min was applied to both groups. Biaxial flexural strength, roughness (Ra and Rz), translucency (TP00), color alteration (ΔE00), Vickers hardness, fracture toughness, residual stresses, and x-ray diffraction analyses were conducted. Statistical analyses were performed with Weibull statistics, Kruskal-Wallis, or ANOVA tests (α = 5%). ResultsSL yielded the highest flexural strength (799.35 MPa), followed by G (662.34 MPa), and C (485.38 MPa). The fracture origin of SL specimens was in the bulk zirconia, while G and C showed fractures starting at the surface. As-sintered reached the highest fracture toughness and hardness. Glaze and borosilicate glass provided surface compressive stresses. Borosilicate glass application led to phase transformation (t→m). SL and G showed the lowest roughness. TP00 and ΔE00 were similar among groups. SignificanceBorosilicate glass improved strength without harming the optical properties of third-generation zirconia. Toughness and roughness provided by the experimental glass were similar to those from commercial glaze.