Abstract
The high-pressure behavior of non-metal nitrides is of special interest for inorganic and theoretical chemistry as well as materials science, as these compounds feature intriguing elastic properties. The double nitride α-BP3 N6 was investigated by in situ single-crystal X-ray diffraction (XRD) upon cold compression to a maximum pressure of about 42 GPa, and its isothermal bulk modulus at ambient conditions was determined to be 146(6) GPa. At maximum pressure the sample was laser-heated, which resulted in the formation of an unprecedented high-pressure polymorph, β-BP3 N6 . Its structure was elucidated by single-crystal XRD, and can be described as a decoration of a distorted hexagonal close packing of N with B in tetrahedral and P in octahedral voids. Hence, β-BP3 N6 is the first nitride to contain PN6 octahedra, representing the much sought-after proof of principle for sixfold N-coordinated P that has been predicted for numerous high-pressure phases of nitrides.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.