Abstract
BackgroundImplants or implantable devices should integrate into the host tissue faster than fibrous capsule formation, in which the design of the interface is one of the biggest challenges. Generally, bioactive materials are not viable for load-bearing applications, so inert biomaterials are proposed. However, the surface must be modified through techniques such as coating with bioactive materials, roughness and sized pores. The aim of this research was to validate an approach for the evaluation of the tissue growth on implants of porous alumina coated with bioactive materials.MethodsPorous alumina implants were coated with 45S5 Bioglass® (BG) and hydroxyapatite (HA) and implanted in rat tibiae for a period of 28 days. Ex vivo resections were performed to analyze osseointegration, along with histological analysis, Scanning Electron Microscopy with Energy Dispersive X-Ray spectroscopy (SEM-EDX) line scanning, radiography and biomechanical testing.ResultsGiven that the process of implant integration needs with the bone tissue to be accelerated, it was then seen that BG acted to start the rapid integration, and HA acted to sustaining the process.ConclusionsInert materials coated with bioglass and HA present a potential for application as bone substitutes, preferably with pores of diameters between 100 μm and 400 μm and, restrict for smaller than 100 μm, because it prevents pores without organized tissue formation or vacant. Designed as functional gradient material, stand out for applications in bone tissue under load, where, being the porous surface responsible for the osseointegration and the inner material to bear and to transmit the loads.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Applied Biomaterials & Functional Materials
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.